EFFECT OF MINOR ALLOYING ADDITION ON PROPERTIES OF Zr-BASED BULK METALLIC GLASS

Authors

  • M. Iqbal Physics Division, Directorate of Science, PINSTECH, P.O. Nilore, Islamabad, Pakistan
  • J. I. Akhtar Physics Division, Directorate of Science, PINSTECH, P.O. Nilore, Islamabad, Pakistan

Abstract

An alloy with composition Zr64Ni17Al11.5Cu7.5 was designed using the criterion of valence electron-atom ratio (1.38) and average atomic size Ra (0.1498 nm). Addition of 2 at. % Ti, V and Pd was carried out in the base alloy. All the alloys were synthesized by Cu mold casting and characterized by SEM, EDS, FESEM, DSC and XRD techniques. Effect of additives on mechanical and thermal properties was studied. The alloys showed good mechanical properties. All the alloys have high fracture strength. Improvement in ductility was achieved with the elemental addition of Ti and V which produced intersecting shear bands in the alloy during compression tests. The calculated thermal parameters indicate good glass-forming ability (GFA) and high thermal stability. Nucleation of liquid droplets within the vein patterns verifies the adiabatic heating theory of BMGs

References

A.R. Yavari, J.J. Lewandowski and J. Eckert,

Mater. Res. Bull.32 (2007) 635.

N. Nishiyama, K. Amiya and A. Inoue, Mate.

Sci. Eng. A 449-451 (2007) 79.

L.Y. Chen, Z.D. Fu, G.Q. Zhang, X.P. Hao,

Q.K. Jiang, X.D. Wang, Q.P. Cao, H. Franz,

Y.G. Liu, H.S. Xie, S.L. Zhang, B.Y. Wang,

Y.W. Zeng and J.Z. Jiang, Phys. Rev. Lett.

(2008) 75501.

G. Kumar, T. Ohkubo, T. Mukai and K. Hono,

Scripta Mater. 57 (2007) 173.

J. Schroers, B. Lohwongwatan, W.L.

Johnson and A. Peker, Mater. Sci. Eng. A

-451 (2007) 235.

A. Inoue, T. Shibata and T. Zhang, Mater.

Trans. JIM 36 (1995) 1420.

A.L. Greer, Nature 366 (1993) 303.

C. Dong, Q. Wang, J.B. Qiang, Y.M. Wang,

N. Jiang, G. Han, Y.H. Li, J. Wu and J.H. Xia,

J. Phys. D: Appl. Phys. 40 (2007) R 273.

C. Dong, Y.M. Wang, J.B. Qiang, D.H. Wang,

W.R. Chen and C.H. Shek, Mater. Trans. 45

(2004) 1177.

M. Iqbal, J.I. Akhter, W.S. Sun, H.F. Zhang,

and Z.Q. Hu, J. Alloy. Compd. 422 (2006)

M. Iqbal, Z.Q. Hu, H.F. Zhang, W.S. Sun and

J.I. Akhter, J. Non-Cryst. Solids 352 (2006)

M. Iqbal, W.S. Sun, H.F. Zhang, J.I. Akhter

and Z.Q. Hu, Mater. Sci. Eng. A 447 (2007)

M. Iqbal, J.I. Akhter, H.F. Zhang and Z.Q. Hu,

J. Mater. Sci. Technol. 23 (2007) 693.

M. Iqbal, J.I. Akhter, H.F. Zhang and Z.Q. Hu,

J. Non-Cryst. Solids 354 (2008) 3291.

M. Iqbal, J.I. Akhter, W.S. Sun , Z.Q. Hu ,

H.F. Zhang, A. Qayyum and W.S. Sun, J.

Non-Cryst. Solids 353 (2007) 2452.

W.H. Wang, Prog. Mater. Sci. 52 (2007) 540.

Z.P. Lu, H. Bei and C.T. Liu, Intermetallics 15

(2007) 618.

Q.J. Chen, J. Shen, D.L. Zhang, H.B. Fan,

J.F. Sun and D.G. McCartney, Mater. Sci.

Eng. A 433 (2006) 155.

Z.Z. Yuan, S.L. Bao, Y. Lu, D.P. Zhang and

L. Yao, J. Alloy. Compd. 459 (2008) 251.

Z.L. Long, G. Xie, H. Wei, J. Peng, P. Zhang

and A. Inoue, Mater. Sci. Eng. A 509 (2009)

-30.

J.B. Qiang, W. Zhang, G.Q. Xie and A. Inoue,

Mater. Trans. JIM 48 (2007) 1789.

J.B. Qiang, W. Zhang and A. Inoue, Scripta

Mater. 55 (2006) 617.

W.H. Jiang, G.J. Fan, F.X. Liu, G.Y. Wang,

H. Choo and P.K. Liaw, J. Mater. Res. 21

(2006) 2164.

L. Liu, C.L. Qiu, M. Sun, Q. Chen, K.C. Chan

and G.K.H. Pang, Mater. Sci. Eng. A 449-451

(2007)193.

L. Zhang, Y.Q. Cheng, A.J. Cao, J. Xu and E.

Ma, Acta Mater. 57 (2009) 1154.

K. Yoshimi, H. Kato, J. Saida and A. Inoue,

Mater. Sci. Forum 539-543 (2007) 2054.

L.F. Liu, L.H. Dai, Y.L. Bai and B.C. Wei, J.

Non-Cryst. Solids 351 (2005) 3259.

Downloads

Published

07-12-2010

How to Cite

[1]
M. Iqbal and J. I. Akhtar, “EFFECT OF MINOR ALLOYING ADDITION ON PROPERTIES OF Zr-BASED BULK METALLIC GLASS”, The Nucleus, vol. 48, no. 1, pp. 67–71, Dec. 2010.

Issue

Section

Articles