EFFECT OF FREQUENCY AND RESISTANCE BY TEMPERATURE VARIATION ON LEAD ZIRCONATE TITANATE PIEZOELECTRIC CERAMICS DISC

Authors

  • R. A. Pasha Department of Mechanical Engineering, University of Engineering and Technology, Taxila, Pakistan
  • G. Raja Department of Electrical Engineering, University of Engineering and Technology, Taxila, Pakistan

Abstract

Lead Zirconate Titanate (PZT) piezoelectric ceramics disc has been analyzed for its output peak- to-peak voltage between a temperature range at variable frequencies and resistances. The temperature range selected was between 70ºC-160ºC. The aim was to determine the real time output peak-to-peak voltage across the thin PZT disc for its reliability analysis at the aforesaid stated conditions. Temperature sensitivity with respect to resistance and frequency was observed. The results indicate that the drop in peak-to-peak voltage was higher at high values of frequencies and resistances. The real time monitoring of PZT disc between 70o C-160o C temperature ranges did not show significant variation in voltage at particular resistance. Insensitivity at this particular temperature range makes these PZT disc reliable for the designing of micro-electromechanical systems within said operating conditions.

References

G. H. Haertling: Journal of American

Ceramics Society 82 (1999) 797.

W. P. Chen, C. P. Chong, H. L. W. Chan and

P. C. K. Liu: Journal of Materials Science and

Engineering:B 99 (2003) 203.

C. H. Xu, C. H. Woo, S. Q Shi and H. L. W

Chan: Current oscillation of piezoelectric

ceramic vibrators driven by a constant high

electric field, Journal of the American

Ceramics Society 88 (2005) 624.

A. Asis, W. Zhang and Y. Xi. Ferroelectrics,

and Frequency Control 50 (2003) 1647.

E. B. Araujo and J. A. Eiras, Mater. Lett. 46

(2000) 265.

M. A. Mohiddon and K. L. Yadav, Advances

in Applied Ceramics 107 (2008) 310.

S. Eitssayeam, U. Intatha, K. Pengpat, G.

Rujiganagul, K.J.D. MacKenzie and

T. Tunkasiri, Current Applied Physics 8

(2008) 266.

H.M.S. Georgion and R. Ben Mrad,

Mechatronics 14 (2004) 667.

J-C. M’ Peko. A. G. Peixoto, E. Jimenez,

and L-M. G-Sager, Journal of Electroceramics 15 (2005) 167.

Downloads

Published

26-08-2011

How to Cite

[1]
R. A. Pasha and G. Raja, “EFFECT OF FREQUENCY AND RESISTANCE BY TEMPERATURE VARIATION ON LEAD ZIRCONATE TITANATE PIEZOELECTRIC CERAMICS DISC”, The Nucleus, vol. 48, no. 3, pp. 191–197, Aug. 2011.

Issue

Section

Articles